Zr-MCM-41的合成及其表征
-
摘要: 以Zr(NO3)4·3H2O为锆源,通过直接合成法得到了Zr-MCM-41介孔材料,考察了不同Zr/Si摩尔比对样品的影响,其中Zr/Si的摩尔比最大为0.25。随着Zr/Si的摩尔比的增加,2θ=2°附近的100晶面的衍射峰强度逐渐降低,当Zr/Si摩尔比大于0.25后得不到介孔Zr-MCM-41材料。对所得样品采用XRD、TG-DTA、N2吸附脱附几种分析方法进行了表征。Abstract: Zr-MCM-41 mesoporous materials were prepared via a direct-synthesis method using Zr(NO3)4·3H2O as a precursor. The samples were characterized with XRD (X-ray Diffraction), TG-DTA (Thermogravimetry-Differential Thermal Analysis) and N2 adsorption. The effects of Zr/Simolar ratio on the Zr-MCM-41 were then investigated. The results show that the peak of 100 near 2θ=2° in XRD patterns becomes weaker with the increase of Zr/Si molar ratio. To obtain the mesoporous Zr-MCM-41, the maximum of Zr/Si molar ratio is 0.25. The BET area of the Zr-MCM-41samples decreases with the increase of Zr/Si ratio, but the pore size keeps as 2.75nm~2.97nm.
-
Key words:
- mesoporous /
- Zr-MCM-41 /
- zirconia /
- zirconium nitrate