Microstructure characteristics and desulphurization of nano-CaCO3 during coal combustion
-
摘要: 为了研究纳米碳酸钙和纳米添加剂在促进燃煤脱硫中的特性，在ZCS-1智能测硫仪中进行纳米碳酸钙脱硫实验研究。结果表明，在炉温900℃、钙硫比为2的条件下，脱硫效率高达90％；1150℃时达到50%以上。三种纳米碳酸钙的脱硫效果明显好于普通碳酸钙。研究还表明，粒径越小，脱硫效果越好；不同煤种对脱硫效率有较大影响，主要和煤中硫分的含量和硫的分布形态有关；温度是决定脱硫效果的主要因素，900℃下效果最好，超过1100℃后效果明显下降。SEM和BET分析结果表明，纳米碳酸钙促进脱硫主要是由于其较为丰富的孔隙结构。添加纳米Al2O3和纳米ZnO都能在一定程度上促进纳米碳酸钙脱硫。其中，纳米Al2O3的效果较好，1150℃能使脱硫效率提高20％左右，达到62%以上。Abstract: The desulphurization performance of nano-CaCO3 during coal combustion was studied by using ZCS-1 intellective sulf-meter, and the effect of additives was also examined. The results show that the desulphurization efficiency is 90% when the temperatures is 900℃ and Ca/S ratio is 2, and more than 50% at 1150℃. Nano-CaCO3 has a higher desulphurization efficiency than the ordinary calcium carbonate. It is indicated that the desulphurization efficiency decreases with the increasing of particle size. The coal type has a great influence on desulphurization due to its different contents and chemical state of sulfur. The temperature is the major factor for the desulphurization. The desulphurization efficiency reaches the highest value at 900℃, but obviously decreases when the temperature is over 1100℃. The SEM and BET results show that nano-CaCO3 can improve the desulphurization process due to its abundant pores. The desulphurization efficiency is increased by adding nano-Al2O3 and nano-ZnO. The nano-Al2O3 additive improves the desulphurization rate by 20% at 1150℃.
-
Key words:
- SO2 /
- nano-CaCO3 /
- desulphurization /
- coal combustion
-
点击查看大图
计量
- 文章访问数: 1905
- HTML全文浏览量: 19
- PDF下载量: 1096
- 被引次数: 0
下载: