MgO/Al2O3吸附剂对CO2动态吸附性能的研究

闻霞; 孙楠楠; 李碧; 李军平; 王峰; 赵宁; 肖福魁; 魏伟; 孙予罕; 任泽厚; 郭金刚; 王志杰; 李庆; 吴志斌

留言板

尊敬的读者、作者、审稿人, 关于本刊的投稿、审稿、编辑和出版的任何问题, 您可以本页添加留言。我们将尽快给您答复。谢谢您的支持!

姓名

邮箱

手机号码

标题

留言内容

验证码

MgO/Al₂O₃吸附剂对CO₂动态吸附性能的研究

闻霞^1,2,
孙楠楠^1|2,
李碧^1|2,
李军平¹,
王峰¹,
赵宁¹,
肖福魁¹,
魏伟^1,,
孙予罕¹,
任泽厚³,
郭金刚³,
王志杰³,
李庆³,
吴志斌³

1.
中国科学院山西煤炭化学研究所| 山西太原 030001;
|2.中国科学院研究生院| 北京 100049; 3.山西潞安矿业(集团)有限责任公司| 山西长治 046204

基金项目: 中国科学院山西煤炭化学研究所知识创新工程领域前沿项目（08SC4A1691）；山西潞安矿业（集团）有限责任公司（08WT181691）

详细信息

作者简介:
闻霞（1983）| 女| 江苏射阳人| 硕士研究生。Email： wxia_123@yahoo.com.cn

通讯作者:
魏伟， Tel:0351-4049612, E-mail: weiwei@sxicc.ac.cn

中图分类号: TQ028
计量
- 文章访问数: 2107
- HTML全文浏览量: 28
- PDF下载量: 1249
- 被引次数: 0
出版历程
- 收稿日期: 2009-08-19
- 修回日期: 2009-11-02
- 刊出日期: 2010-04-30

Dynamic adsorption study of CO₂adsorption by MgO/Al₂O₃

1.
Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001, China|
|2.Graduate University of Chinese Academy of Sciences, Beijing 100049, China|

摘要

摘要: 以γ- Al₂O₃为载体，采用等体积浸渍法制取MgO/Al₂O₃吸附剂，利用BET、XRD等表征手段对吸附剂进行表征；并通过固定床测量穿透曲线的方法研究其对CO2动态吸附性能的影响，考察了MgO负载量、吸附温度、气体流量等因素对吸附剂吸附CO₂性能的影响，同时还通过多次吸脱附实验考察MgO/Al₂O₃吸附剂的稳定性和再生能力。结果表明，MgO负载量为10%的吸附剂，吸附温度在50℃左右，流量为45mL/min动态吸附量最大；经数次循环后材料的结构性质和吸附性能未见明显变化，可再生性能比较优异，是一种潜在的可工业化应用的CO₂吸附剂。
- CO₂ /
- 固定床 /
- 吸附量 /
- 穿透曲线 /
- MgO/Al₂O₃
Abstract: A MgO/Al₂O₃ adsorbent prepared with impregnation method was characterized by using N₂-adsorption and XRD, and its CO₂ kinetic sorption properties were studied by means of breakthrough analysis in a fixed bed flow adsorber. The effects of MgO loadings, adsorption temperatures and gas flow rates were investigated. The stability and regenerative abilities were studied by cyclic experiment. The results indicated that the optimal loading of MgO was 10%, the maximal adsorption capacities were achieved when the temperature was 50℃ and the gas flow rate was 45mL/min. The texture properties as well as the adsorption capacity were maintained in multiple cycles, thus the MgO/Al₂O₃ adsorbent could be considered as a potential CO₂ adsorption in industrial application.
- carbon dioxide /
- fixed-bed /
- adsorption capacities /
- breakthrough curves /
- MgO/Al₂O₃