Effect of reduction temperature on performance of double mesoporous Co-based catalysts in Fischer-Tropsch synthesis
-
摘要: 通过等体积浸渍法制备了双介孔钴基催化剂,采用XRD、BET、SEM、H2-TPR等手段考察了催化剂的性质,并研究了还原温度对催化剂结构及费托合成催化性能的影响。结果表明,随着还原温度的提高,催化剂活性位增加,活性增加,但增加到一定程度后活性降低,而甲烷选择性随着还原温度的提高逐渐增加,这是反应过程中催化剂表面存在的钴氧化物,使得水煤气反应变得活跃,烃产物移向低碳烃。Abstract: The double mesoporous Co-based catalysts were prepared by incipient-wetness impregnation method, which were characterized by the technology of XRD, BET, SEM and H2-TPR. And the influences of reduction temperature on the structure and performance of the catalysts in Fischer-Tropsch were investigated. The result showed that with the increase of reduction temperature, the active sites of catalysts increased, and the activity increased. After the activity reached a certain level, it began to decline. And the methane selectivity increased with the increase of reduction temperature. The related reactive performance might be due to the cobalt oxides on the surface of catalysts formed in the reaction, which made the water gas shift reaction become active, and the hydrocarbon products moved to low hydrocarbons.
-
Key words:
- Fischer-Tropsch synthesis /
- double mesoporous /
- reduction temperature /
- Co-based catalyst
-
JONGSOMJIT B, GOODWIN J G. Co-support compound formation in Co/Al2O3 catalysts: Effect of reduction gas containing CO[J]. Catal Today, 2002, 77(3): 191-204. 王野, 康金灿, 张庆红. 费托合成催化剂的研究进展[J]. 石油化工, 2009, 38(12): 1255-1263. (WANG Ye, KANG Jin-can, ZHANG Qing-hong, Research advances in catalysts for Fischer-Tropsch synthesis[J]. Petrochemical Technology, 2009, 38(12): 1255-1263.) KHODAKOV A Y, BECHARA R, GRIBOVAL-CONSTANT A. Fischer-Tropsch synthesis over silica supported cobalt catalysts: Mesoporous structure versus cobalt surface density[J]. Appl Catal A: Gen, 2003, 254(2): 273-288. KHODAKOV A Y, GRIBOVAL-CONSTANT A, BECHARA R, VILLAIN F. Pore-size control of cobalt dispersion and reducibility in mesoporous silicas[J]. J Phys Chem B, 2001, 105(40): 9805-9811. KHODAKOV A Y, GRIBOVAL-CONSTANT A, BECHARA R, ZHOLOBENKO V L. Pore size effects in Fischer Tropsch synthesis over cobalt-supported mesoporous silicas[J]. J Catal, 2002, 206(2): 230-241. WANG Y L, CHEN J G, FANG K G. Natural gas conversion Viii//Proceedings of the 8th Natural Gas Conversion Symposium. Natal, Brazil, 2007: 103-109. SHINODA M, ZHANG Y, YONEYAMA Y, HASEGAWA K, TSUBAKI N. New bimodal pore catalysts for Fischer-Tropsch synthesis[J]. Fuel Process Technol, 2004, 86(1): 73-85. ZHANG Y, KOIKE M, YANG R Q, HINCHIRANAN S, VITIDSANT T, TSUBAKI N. Multi-functional alumina-silica bimodal pore catalyst and its application for Fischer-Tropsch synthesis[J]. Appl Catal A: Gen, 2005, 292: 252-258. ZHANG Y, KOIKE M, TSUBAKI N. Preparation of alumina-silica bimodal pore catalysts for Fischer-Tropsch synthesis[J]. Catal Lett, 2005, 99(3/4): 193-198. WANG J G, LI D B, HOU B, JIA L T, CHEN J G, SUN Y H. Textural structure of Co-based catalysts and their performance for Fischer-Tropsch synthesis[J]. Catal Lett, 2010, 140(3/4): 127-133. VANSTEEN E, SEWELL G S, MAKHOTHE R A, MICKLETHWAITE C, MANSTEIN H, DELANGE M, OCONNOR C T. TPR study on the preparation of impregnated Co/SiO2 catalysts[J]. J Catal, 1996, 162(2): 220-229. SONG D C, LI J L. Effect of catalyst pore size on the catalytic performance of silica supported cobalt Fischer-Tropsch catalysts[J]. J Mol Catal A: Chem, 2006, 247(1/2): 206-212. O'SHEA V A D P, HOMS N, FIERRO J L G, DE LA PISCINA P R. Structural changes and activation treatment in a CO/SiO2 catalyst for Fischer-Tropsch synthesis[J]. Catal Today, 2006, 114(4): 422-427. DUCREUX O, LYNCH J, REBOURS B, ROY M, CHAUMETTE P. In situ characterisation of cobalt based Fischer-Tropsch catalysts: A new approach to the active phase[J]. Stud Sur Sci Catal, 1998, 119: 125-130. IGLESIA E. Design, synthesis, and use of cobalt-based Fischer-Tropsch synthesis catalysts[J]. Appl Catal A: Gen, 1997, 161(1/2): 59-78.
点击查看大图
计量
- 文章访问数: 1136
- HTML全文浏览量: 22
- PDF下载量: 642
- 被引次数: 0