Morphological and interfacial characterization of molten slags on the refractory surface
-
摘要: 研究了碱酸比不同的3种熔融煤灰(A、J1和J2)在莫来石和刚玉两种耐火材料上的界面特性。结果表明,A对莫来石和刚玉都有很好的润湿性,而J1和J2对这两种耐火材料则经历由不完全润湿到润湿的过程。熔渣与耐火材料(S-R)界面宽度随着接触角减小而增大。从灰渣开始熔融至1 520 ℃,熔融煤灰J1在耐火材料表面上的接触角随着倾角的增加而减小;当倾角为20°时,其接触角突然增大。SEM-EDS分析表明,由于界面反应,A比J1更容易渗透进入耐火材料内部。对于碱酸比不同的煤灰,渗透和酸碱反应是熔渣对耐火材料腐蚀的关键。Abstract: The interfacial properties between three types of coal slags (A, J1 and J2 with various base/acid ratio) and two refractory materials (mullite and corundum) were studied. The results indicate that the slag A has good wettability on both of refractory materials. While, the slags J1/J2 have experienced the process from incomplete wetting to whole wetting. The contact angles decrease with increasing of interface width of slag and refractory materials (S-R). The contact angles of J1 on mullite decrease with increasing of inclination angles from deformation temperature to 1 520 ℃, but significantly increase when the inclination angle is 20°. The SEM-EDS analysis show that the quantity of slag A permeating into the refractory material is more than that of J1 slags because of interfacial reaction. The infusion and acid-base reactions are the key factors for the refractory corrosion.
-
Key words:
- refractory material /
- slag /
- erosion /
- interface
-
SUKUL G, BALARAMAKRISHNA P V. A review of refractory linings for gasification reactors[J]. J Aust Ceram Soc, 2014, 50(2): 83-92. GEHRE P, ANEZIRIS C G, VERES D, PARR C, FRYDA H, NUROTH M. Improved spinel-containing refractory castables for slagging gasifiers[J]. J Eur Ceram Soc, 2013, 33(6): 1077-1086. SUKUL G, BALARAMAKRISHNA P V, HERWADKAR S V. Investigation of refractory lining in hot gas generators[J]. Inter Ceram, 2010, 59(3/4): 209-212. GEHRE P, ANEZIRIS C G. Investigation of slag containing refractory materials for gasification processes[J]. J Eur Ceram Soc, 2012, 32(16): 4051-4062. KWONG K, PETTY A, BENNETT J, KRABBE R, THOMAS H. Wear mechanisms of chromia refractories in slagging gasifiers[J]. Int J Appl Ceram Technol, 2007, 4(6): 503-513. BENNET J P, KWONG K. Refractory liner materials used in slagging gasifiers[J]. Refract Appl News, 2004, 9(5): 20-25. TABER W A. Refractories for gasification[J]. Refract Appl News, 2003, 8(4): 18-22. 周俊虎, 赵晓辉, 刘建中, 杨卫娟, 黄镇宇, 岑可法. 锅炉内卫燃带上高熔点灰渣沉积机理分析[J]. 中国电机工程学报, 2008, 28(14): 20-26. (ZHOU Jun-hu, ZHAO Xiao-hui, LIU Jian-zhong, YANG Wei-juan, HUANG Zhen-yu, CEN Ke-fa. Analysis on deposition mechanism of ash with high ash fusion temperatures on the heat-insulation layer in boiler[J]. Chin Soc for Elec Eng, 2008, 28(14): 20-26.) 高峰, 单晓伟. 煤灰在不同耐火砖表面的润湿性与腐蚀性研究[J]. 燃料化学学报, 2012, 40(7): 769-775. (GAO Feng, SHAN Xiao-wei. Wettability and erodibility of coal ash on the surface of different refractories[J]. J Fuel Chem Technol, 2012, 40(7): 769-775.) NAKANO J, SRIDHAR S, BENNETT J, KWONG K, MOSS T. Interactions of refractory materials with molten gasifier slags[J]. Int J Hydrogen Energy, 2011, 36(7): 4595-4604. KENNETH K T, BENNETT J, SRIDHAR S. Effect of temperature gradient on industrial gasifier coal slag infiltration into alumina refractory[J]. J Am Ceram Soc, 2011, 94(12): 4507-4515. RAWERS J, IVERSON L, COLLINS K. Initial stages of coal slag interaction with high chromia sesquioxide refractories[J]. J Mater Sci, 2002, 37(3): 531-538. 陆佩文. 无机材料科学基础[M]. 武汉: 武汉理工大学出版社, 1996, 117. (LU Pei-wen. Fundamentals of inorganic materials science[M]. Wuhan: Wuhan University of Technology Press, 1996, 117. ZHANG J Y, ZHAO Y C, WEI C, YAO B, ZHENG C G. Mineralogy and microstructure of ash deposits from the Zhuzhou coal-fired power plant in China[J]. Int J Coal Geol, 2010, 81(4): 309-319.
点击查看大图
计量
- 文章访问数: 395
- HTML全文浏览量: 27
- PDF下载量: 605
- 被引次数: 0