Influence of Co-Ce co-doping on photocatalytic DeNOx of TiO2 catalyst at room temperature
-
摘要: 将钛酸丁酯作为Ti源,硝酸铈作为Ce源,硝酸钴作为Co源,采用溶胶-凝胶水热法制备出Ce-TiO2和Ce-Co-TiO2催化剂。对所制备的改性TiO2催化剂进行BET、XRD、SEM、UV-vis、XPS、NH3-TPD等表征分析测试,并以NO为研究对象对不同改性TiO2催化剂进行了可见光催化实验,探究改性TiO2催化剂脱除NO的效率。结果表明,以硝酸铈为Ce源(掺杂物质的量比1%),硝酸钴为Co源(掺杂物质的量比5%),在水热反应温度为160 ℃的条件下反应24 h后在200 ℃下煅烧得到的Ce(1%)-Co(5%)-TiO2催化剂性能最好。其对浓度为762 μg/m3的NO可见光催化效率高达92.69%,在浓度提高至1148 μg/m3时在室温下的可见光催化效率仍可达85.94%,与纯TiO2相比效率提高了近50%。而且Ce(1%)-Co(5%)-TiO2催化剂的抗硫性能与连续使用次数都比商用催化剂(掺杂有V2O5的商用TiO2)好。
-
关键词:
- Ce-Co-TiO2 /
- 脱硝 /
- 室温 /
- 可见光催化
Abstract: Ce-TiO2 and Ce-Co-TiO2 powders were prepared by the sol-gel hydrothermal method with butyl titanate as the source of Ti, cerium nitrate as the source of Ce, cobalt nitrate for Co source. The modified TiO2 catalysts were characterized with BET, XRD, SEM, UV-vis, XPS and NH3-TPD. The NO reduction efficiency by visible light over the modified TiO2 catalysts was carried out. The experimental results show that the catalyst Ce (1% molar)-Co (5% molar)-TiO2 prepared under the conditions of 24 h hydrothermal synthesis at 160 and 200 ℃of calcination showed the best performance. At room temperature, the visible light catalytic efficiency of the catalyst reached 92.69% when the NO initial concentration was 762 μg/m3. When the NO initial concentration was 1148 μg/m3, the visible light catalytic efficiency could still reach 85.94%, which was improved by nearly 50% compared with pure TiO2. Moreover, it was found that in the resistance of SO2 and continuous usage, the efficiency of the Ce (1%)-Co (5%)-TiO2 catalyst was better than the commercial catalysts (TiO2 with V2O5 doping).-
Key words:
- Ce-Co-TiO2 /
- denitration /
- room temperature /
- visible light catalysis
-
表 1 共掺不同元素的催化效率
Table 1 Catalytic efficiency of different element doping (initial concentration of NO:1148 μg/m3)
Zr-Ce(1%)-TiO2 Efficiency/% Mn-Ce(1%)-TiO2 Efficiency/% Co-Ce(1%)-TiO2 Efficiency/% 0.5% 54.55 0.5% 55.41 1% 66.67 1.0% 71.43 1.0% 60.29 3% 71.64 1.5% 72.73 1.5% 66.15 5% 85.94 2.0% 75.76 2.0% 66.70 7% 64.71 表 2 样品表面结构数据
Table 2 Surface structural data of the samples
Sample ABET/(m2·g-1) rp/nm vm/(cm3·g-1,STP) vp/(cm3·g-1) TiO2 89.5 10.98 20.87 0.25 Ce(1%)-TiO2 104.9 10.10 24.09 0.27 Ce(1%)-Co(5%)-TiO2 126.1 10.40 25.88 0.33 表 3 不同类型催化剂光催化反应氧化率
Table 3 Photocatalytic oxidation rate of different types of catalysts
Sample Commercial catalyst TiO2 Ce(1%)-TiO2 Ce(1%)-Co(5%)-TiO2 Oxidation rate/% 18.35 16.37 20.31 23.45 -
[1] 中国电力企业联合会.中国电力行业年度发展报告[M].北京:中国市场出版社, 2018.China Electricity Council. China Power Industry Annual Development Report[M]. Beijing:China Market Press, 2018. [2] 国家环境保护总局.火电厂大气污染物排放标准[S].State Environmental Protection Administration. Thermal power plant emission standards for atmospheric pollutants[S]. [3] ZHANG D R, LIU H L, HAN S Y, PIAO W X. Synthesis of Sc and V-doped TiO2 nanoparticles and photodegradation of rhodamine-B[J]. J Ind Eng Chem, 2013, 19(6):1838-1844. doi: 10.1016/j.jiec.2013.02.029 [4] REDDY B M, KHAN A. Structural characterization of CeO2-TiO2 and V2O5/CeO2-TiO2 catalysts by Raman and XPS techniques[J]. J Phys Chem B, 2003, 107(22):5162-5167. doi: 10.1021/jp0344601 [5] 袁春华, 谢英娜.钴掺杂二氧化钛光催化剂制备及光催化活性[J].无机盐工业, 2011, 43(11):31-33. doi: 10.3969/j.issn.1006-4990.2011.11.010YUAN Chun-hua, XIE Ying-na. Preparation of cobalt-doped titania photocatalysts and photocatalytic activity thereof[J].Inorg Chem Ind, 2011, 43(11):31-33. doi: 10.3969/j.issn.1006-4990.2011.11.010 [6] LI X H, ZHANG S L, JIA Y, LIU X X, ZHONG Q. Selective catalyticoxidation of NO with O2 over Ce-doped MnOx/TiO2 catalysts[J]. Nat Gas Chem, 2012, 1(1):17-24. http://www.cqvip.com/QK/84213X/201201/40867454.html [7] 宋林云, 吴玉程, 李云, 叶敏, 谢挺, 黄新民.介孔Co-TiO2的制备及其光催化性能研究[J].武汉理工大学学报, 2007, 39(10):66-69. http://d.old.wanfangdata.com.cn/Periodical/gncl200801010SONG Lin-yun, WU Yu-cheng, LI Yun, YE Min, XIE Ting, HUANG Xin-min. Preparation and photocatalytic performance of mesoporous Co-TiO2[J]. J Wuhan Univ Technol, 2007, 39(10):66-69. http://d.old.wanfangdata.com.cn/Periodical/gncl200801010 [8] 李伟, 张成, 李鑫, 谭鹏, 方庆艳, 陈刚. Ho掺杂对Mn-Ce/TiO2低温SCR催化剂的脱硝性能影响[J].燃料化学学报, 2017, 45(12):1508-1513. doi: 10.3969/j.issn.0253-2409.2017.12.013LI Wei, ZHANG Cheng, LI Xin, TANG Peng, FANG Qing-yan, CHEN Gang. Influence of Ho doping on the deNOx performance of Mn-Ce/TiO2 low temperature SCR catalyst[J]. J Fuel Chem Technol, 2017, 45(12):1508-1513. doi: 10.3969/j.issn.0253-2409.2017.12.013 [9] 徐文青, 赵俊, 王海蕊, 朱廷钰, 李鹏, 荆鹏飞. TIO2负载Mn-Co复合氧化物催化剂上NO催化氧化性能[J].物理化学学报, 2013, 29(2):385-390. doi: 10.3866/PKU.WHXB201212031XU Wen-qing, ZHAO Jun, WANG Hai-xin, ZHU Ting-yu, ZHAO Peng, JING Peng-fei. Catalytic oxidation activity of NO on TIO2-supported Mn-Co composite oxide catalysts[J]. Acta Phys-Chim Sin, 2013, 29(2):385-390. doi: 10.3866/PKU.WHXB201212031 [10] 陈爽, 姚淑华, 石中亮.花瓣状铈掺杂纳米TiO2光催化剂的制备及其光催化活性[J].中南大学学报(自然科学版), 2016, 47(5):1487-1493. http://d.old.wanfangdata.com.cn/Periodical/zngydxxb201605005CHEN Shuang, YAO Shu-hua, SHI Zhong-liang. Preparation and photocatalytic activity of petal-like doped nano TiO2 photocatalyst using hydrothermal method[J]. J Cent S Univ (Sci Technol), 2016, 47(5):1487-1493. http://d.old.wanfangdata.com.cn/Periodical/zngydxxb201605005 [11] MURPHY A. Band-gap determination from diffuse reflectance measurements of semiconductor films, and application to photoelectrochemical water-splitting[J]. Sol Energy Mater Sol Cells, 2007, 91(14):1326. doi: 10.1016/j.solmat.2007.05.005 [12] SENTHIL R A, THEERTHAGIRI J, SELVI A, MADHAVAN J. Synthesis and characterization of low-cost g-C3N4/TiO2 composite with enhanced photocatalytic performance undervisible-light irradiation[J]. Opt Mate, 2017, 64:533-539. doi: 10.1016/j.optmat.2017.01.025 [13] 陈其凤, 姜东, 徐耀, 吴东, 孙予罕.溶胶-凝胶-水热法制备Ce-Si/TiO2及其可见光催化性能[J].物理化学学报, 2009, 25(4):617-623. doi: 10.3866/PKU.WHXB20090412CHEN Qi-feng, JIANG Dong, XU Yao, WU Dong, SUN Yu-han. Preparation of Ce-Si/TiO2 by sol-gel hydrothermal method and its photocatalytic performance[J]. Acta Phys-Chim Sin, 2009, 25(4):617-623. doi: 10.3866/PKU.WHXB20090412 [14] 张璐, 谢健, 李国强, 张洪良.掺杂Ce4+对溶胶-凝胶法制备二氧化钛薄膜的结构和光催化特性的影响[J].半导体光电, 2013, 34(1):98-102. http://d.old.wanfangdata.com.cn/Periodical/bdtgd201301024ZHANG Lu, XIE Jian, LI Guo-qaing, ZHANG Hong-liang. Effect of Ce4+-doping on structural and photocatalytic properties of sol-gel prepared titanium dioxide thin-films[J]. Semicond Optoelectron, 2013, 34(1):98-102. http://d.old.wanfangdata.com.cn/Periodical/bdtgd201301024 [15] 祝豪杰, 武军. Co掺杂锐钛矿型TiO2可见光催化特性机理研究[J].杭州电子科技大学学报, 2012, 32(5):21-24. doi: 10.3969/j.issn.1001-9146.2012.05-006ZHU Hao-jie, WU Jun. The visible light catalytic properties and mechanism of Co co-doped anatase TiO2[J]. J Hangzhou Elect Sci Technol Univ, 2012, 32(5):21-24. doi: 10.3969/j.issn.1001-9146.2012.05-006 [16] 冯云桑, 刘少光, 陈成武, 吴进明, 徐玉松. Co-Ce氧化物对MnOx/TiO2低温SCR脱硝催化剂的影响[J].材料热处理学报, 2014, 35(6):26-33. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=jsrclxb201406005FENG Yun-Sang, LIU Shang-guang, CHEN Cheng-wu, WU Jin-ming, XU Yu-song. Effect of doping Co-Ce oxide on MnOx/TiO2 low-temperature SCR DeNOx catalys[J]. Trans Mater Heat Treat, 2014, 35(6):26-33. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=jsrclxb201406005 [17] 于国峰, 韦彦斐, 金瑞奔, 朱虹, 顾震宇, 潘理黎. Mn-Ce-Co/TiO2催化剂低温脱硝活性研究[J].环境科学学报, 2012, 32(7):1743-1749. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=hjkxxb201207027YU Guo-feng, WEI Yan-pei, JIN Rui-ben, ZHU Hong, GU Zhen-yu, PAN Li-li. The research of Mn-Ce-Co/TiO2 catalyst denitration on low temperature[J]. J Environ Sci-China, 2012, 32(7):1743-1749. http://www.wanfangdata.com.cn/details/detail.do?_type=perio&id=hjkxxb201207027 [18] 张前程, 张凤宝, 张国亮, 张晓萍.超细钴掺杂二氧化钛的制备、表征及气相光催化性能[J].燃料化学学报, 2004, 32(2):240-243. doi: 10.3969/j.issn.0253-2409.2004.02.023ZHANG Qian-cheng, ZHANG Feng-bao, ZHANG Guo-liang, ZHANG Xiao-ping. Preparation and characterization of ultrafine TiO2 doped with Co and its performance in gas-phase photocatalytic oxidation[J]. J Fuel Chem Technol, 2004, 32(2):240-243. doi: 10.3969/j.issn.0253-2409.2004.02.023 [19] LI J Y, SONG Z X, NING P, ZHANG Q L, LIU X, LI H, HUANG Z Z. Influence of calcination temperature on selective catalytic reduction of NOx with NH3 over CeO2-ZrO2-WO3 catalyst[J]. J Rare Earths, 2015, 33(7):726-735. doi: 10.1016/S1002-0721(14)60477-4 [20] 廖永进, 张亚平, 余岳溪, 李娟, 郭婉秋, 汪小蕾. MnOx/WO3/TiO2低温选择性催化还原NOx机理的原位红外研究[J].化工学报, 2016, 67(12):5031-5039. http://www.cnki.com.cn/Article/CJFDTotal-HGSZ201612015.htmLIAO Yong-jin, ZHANG Ya-ping, YU Yue-xi, LI Juan, GUO Wang-qiu, WANG Xiao-lei. In situ FT-IR studies on low temperature NH3-SCR mechanism of NOx over MnOx/WO3/TiO2 catalyst[J]. CIESC J, 2016, 67(12):5031-5039. http://www.cnki.com.cn/Article/CJFDTotal-HGSZ201612015.htm [21] 刘晓飒, 陈淑俊, 赵铁英, 李德艳, 白小鸽, 李留琴.吡啶-热脱附-红外法确定催化剂酸性[J].工业催化, 2015, 23(10):817-820. doi: 10.3969/j.issn.1008-1143.2015.10.018LIU Xiao-da, CHEN Shu-jun, ZHAO Tie-ying, LI De-yan, BAI Xiao-ge, LI Liu-qin. Pyridine-thermal desorption-infrared method for characterization catalyst acidity[J]. Ind Catal, 2015, 23(10):817-820. doi: 10.3969/j.issn.1008-1143.2015.10.018 [22] 束韫, 张凡, 王洪昌, 朱金伟. SO2和H2O对CeO2/TiO2/堇青石催化剂选择催化还原NOx性能的影响[J].燃料化学学报, 2014, 42(9):1111-1118. http://www.ccspublishing.org.cn/article/id/100033204SU Wen, ZHANG Fan, WANG Hong-chang, ZHU Jin-wei. The influence of SO2 and H2O for selective catalytic reduction of NOx of CeO2/TiO2/cordierite[J]. J Fuel Chem Technol, 2014, 42(9):1111-1118. http://www.ccspublishing.org.cn/article/id/100033204 [23] 彭莉莉. CoOx/ZrO2催化氧化NO性能研究[D].湘潭: 湘潭大学, 2012. http://cdmd.cnki.com.cn/Article/CDMD-10530-1013302667.htmPENG Li-li. The research of CoOx/ZrO2 catalytic oxidation NO[D]. Xiangtan: Xiangtan University, 2012. http://cdmd.cnki.com.cn/Article/CDMD-10530-1013302667.htm [24] YU H, WEI W, QIAN Z, CAO J J, HUANG R J, HO W K, SHUN C L. In situ fabrication of α-Bi2O3/(BiO)2CO3 nanoplate heterojunctions with tunable optical property and photocatalytic activity[J]. Sci Reports, 2016, 6(2):34-35. http://www.ncbi.nlm.nih.gov/pubmed/26997545 [25] LI H, SHI J G, ZHAO K, ZHANG L Z. Sustainable molecular oxygen activation with oxygen vacancies on the {001} facets of BiOCl nanosheets under solar light[J]. Nanoscale, 2014, 6(23):14168-14173. doi: 10.1039/C4NR04810E [26] 魏凤玉, 倪良锁.硼硫共掺杂TiO2的光催化性能及掺杂机理[J].催化学报, 2007, 28(10):905-909. doi: 10.3321/j.issn:0253-9837.2007.10.014WEI Feng-yu, Ni Liang-suo. Photocatalytic performance and doping mechanism of B-S Co-doped TiO2[J]. Chin J Catal, 2007, 28(10):905-909. doi: 10.3321/j.issn:0253-9837.2007.10.014